[1]赵 文a,徐一诺b,郎秀瑞a,等.多巴胺和γ-氨丙基三乙氧基硅烷共修饰纳米金刚石及硅橡胶复合材料的制备与导热性能[J].合成橡胶工业,2024,2:168.
　ZHAO Wena,XU Yi-nuob,LANG Xiu-ruia,et al.Preparation and thermal conductivity of dopamine and γ-aminopropyl triethoxysilane co-modified nano-diamond and silicone rubber composites[J].China synthetic rubber industy,2024,2:168.
点击复制

多巴胺和γ-氨丙基三乙氧基硅烷共修饰纳米金刚石及硅橡胶复合材料的制备与导热性能(PDF)

《合成橡胶工业》[ISSN:1000-1255/CN:62-1036/TQ]

期数:
2024年2期
页码:
168
栏目:
出版日期:
1900-01-01

文章信息/Info

Title:
Preparation and thermal conductivity of dopamine and γ-aminopropyl triethoxysilane co-modified nano-diamond and silicone rubber composites
文章编号:
1000-1255（2024）02-0160-07
作者:
赵 文a; 徐一诺b; 郎秀瑞a; 丁珂珂a; 曹 兰a; 宗成中a
青岛科技大学 a.高分子科学与工程学院；b.中德工程学院，山东 青岛 266042
Author(s):
ZHAO Wena;  XU Yi-nuob; LANG Xiu-ruia;  DING Ke-kea;  CAO Lana;  ZONG Cheng-zhonga*
a. School of Polymer Science and Engineering; b. Sino-German College of Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
关键词:
硅橡胶; 纳米金刚石; 聚多巴胺; 氨基硅烷; 表面修饰; 热导率
Keywords:
-
分类号:
-
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2024.02.0168
文献标识码:
-
摘要:
首先利用多巴胺的氧化自聚合在纳米金刚石（ND）表面包覆聚多巴胺（PDA），以引入羟基、氨基等活性基团，然后在ND上继续接枝γ-氨丙基三乙氧基硅烷（KH 550）得到ND-PDA-KH 550，再与硅橡胶（SiR）发生化学反应制得ND-PDA-KH 550/SiR复合材料。结果表明，在ND上接枝PDA和KH 550可有效改变ND表面的物理化学性质，提高ND与SiR基体的界面相互作用，降低界面热阻，从而显著提高复合材料的导热性能；当ND质量分数为6%时，ND-PDA-KH 550/SiR复合材料在25，50，75，100 ℃下的热导率分别为0.340，0.398，0.484，0.586 W/（m·K），比纯SiR材料的热导率分别提高了94.3%、118.7%、161.6%和211.7%。
Abstract:
Elastomer thermal interface materials were mainly prepared by adding thermal conductive particles to silicone rubber(SiR). Nano-diamond (ND) had high thermal conductivity and insulation properties, making it an ideal thermal conductive filler. Nevertheless, ND was prone to agglomeration and difficult to disperse in SiR.　In this work, ND was modified with polydopamine (PDA) and γ-aminopropyl triethoxysilane (KH 550) to improve its dispersion in SiR and its interfacial interaction with. Then the interfacial thermal resistance reduced and the thermal conductivity of the composite improved. Fig 1 showed the infrared spectra of ND, ND-KH 550 and ND-PDA-KH 550. The significant absorption peaks of unmodified ND at 3 200-3 600 cm-1 might be vibration absorption peaks of —OH and H—OH. At 1 624 cm-1, there was a bending vibration absorption peak of —OH or H—OH, indicating the presence of some hydroxyl groups on the ND surface or adsorbed water. The absorption peak position of ND-KH 550 was the same as that of ND, which meaned that KH 550 could not effectively modify ND without dopamine. After treatment with dopamine and KH 550, Si—O—Si ben-ding vibration absorption peak appeared at 463 cm-1, Si—O bond symmetric and asymmetric stretching vibration absorption peaks appeared at 763 cm-1 and 1 049 cm-1, Si—C stretching vibration absorption peak appeared at 695 cm-1, Si—H deformation vibration absorption peak appeared at 914 cm-1. The appearance of the new absorption peak indicated that PDA had successfully grafted silane coupling agent KH 550 onto the surface of ND as a “bridge”.■Fig 1 FTIR spectra of ND, ND-KH 550 and ND-PDA-KH 550　Fig 2 showed the thermal conductivity of SiR, ND/SiR, ND-KH 550/SiR and ND-PDA-KH 550/SiR at different temperatures. The thermal conductivities of SiR, ND/SiR and ND-KH 550/SiR composites were not sensitive to temperature. As the temperature increased, there were only a slight variation in the thermal conductivity. The thermal conductivity of ND-KH 550/SiR composite prepared by treating ND with only KH 550 was almost the same as that of ND/SiR at any temperature, indica-ting that there were no functional groups on the surface of ND that could react with KH 550.■Sample: ○—SiR; ●—ND/SiR; △—ND-KH 550/SiR; ▲—ND-PDA-KH 550/SiRFig 2 Thermal conductivities of SiR, ND/SiR, ND-KH 550/SiR and ND-PDA-KH 550/SiR at different temperatures　However, the thermal conductivity of ND-PDA-KH 550/SiR composite prepared by modifying ND with PDA and KH 550, and then adding it to silicone rubber, increased significantly with increasing temperature. The thermal conductivity of ND-PDA-KH 550/SiR was 0.340 W/(m·K) at 25 ℃ and 0.586 W/(m·K) at 100 ℃, which increased by 72.4%. Modifying ND with dopamine and KH 550 can improve the dispersion of ND in silicone rubber and the compatibility between ND and silicone rubber, reducing the interface thermal resistance and phonon scattering. The increase of temperature accelerated the movement of phonons and improved the efficiency of heat transfer, which showed that the thermal conductivity of the composite increased with the increase of temperature. At 25 ℃, 50 ℃, 75 ℃ and 100 ℃, the thermal conductivity of ND-PDA-KH 550/SiR composites with 6% ND increased by 94.3%, 118.7%, 161.6% and 211.7% respectively, compared with that of pure SiR.