Title:
Study on emulsifying technology of brominated butyl rubber
文章编号:
1000-1255（2022）06-0474-05
作者:
李洪阳; 熊 鹰; 何 牧; 周晓龙鄢
华东理工大学化工学院 石油加工研究所， 上海 200237
Author(s):
LI Hong-yang;  XIONG Ying;  HE Mu;  ZHOU Xiao-long
Research Institute of Petroleum Processing， School of Chemical Engineering, East China University of Science and Technology, Shanghai 200237, China
关键词:
溴化丁基胶乳; 乳化剂; 乳化工艺; 蒸馏; 破乳率; 破乳成膜
Keywords:
brominated butyl rubber latex;  emulsifier;  emulsification process;  distillation;  demulsification rate;  emulsion film
分类号:
TQ 333.6
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2022.06.0474
文献标识码:
A
摘要:
采用乳化工艺制备了溴化丁基橡胶（BIIR）胶乳，研究了乳化剂种类、BIIR正己烷溶液浓度、乳化时间、乳化转速、胶乳体系pH值及蒸馏方式对BIIR胶乳的影响。结果表明，乳化BIIR的最佳条件为：BIIR正己烷溶液中BIIR质量分数为15.00%，体系pH值调节至11～12，高速剪切乳化时间为30 min，高剪转速为5 500～6 000 r/min，采用负压（压力为-0.04 MPa）旋转蒸馏，所得BIIR胶乳的蒸馏破乳率较低，且总固物质量分数可以达到45.00%以上；使用质量分数为20%的氯化钙溶液破乳成膜效果最佳。
Abstract:
Brominated butyl rubber (BIIR) latex was prepared by emulsification process, and the effects of emulsifier type, concentration of BIIR n-hexane solution, emulsification time, emulsification speed, pH value of latex system and distillation method on BIIR latex were studied. The results showed that the optimal conditions for emulsifying BIIR were that mass fraction of BIIR of 15.00% in n-hexane solution, the pH value of the latex system of 11-12, the high-speed shear emulsification time of 30 min, the high-speed shear speed of 5 500-6 000 r/min, and the negative-pressure rotary distillation (pressure of -0.04 MPa), and the demulsification rate of the resulting BIIR latex was low and mass fraction of the total solid could reach more than 45.00%. The best demulsification and film-forming effect was obtained by using mass fraction of 20% calcium chloride solution.

参考文献/References

［1］ 房尔园. 溴化丁基橡胶的结构与性能研究［D］. 南京：南京理工大学， 2013.［2］ 刘芸， 段芳， 曹兰， 等. 稀土系聚异戊二烯胶乳乳化工艺探讨［J］. 合成橡胶工业， 2018， 41（1）： 23-26.［3］ Holmberg K， Jonsson B， Kronberg B， et al. Polymers in Solution［M］. New Jersey： John Wiley & Sons， 2003： 223-226. ［4］ Chao Chizheng， Lin Gwogeng， Tsai Hsiehchih， et al. Isobutylene-isoprene rubber/layered silicate nanocomposites prepared using latex method： Direct casting versus melt mixing after coagulation［J］. Journal of Reinforced Plastics and Composites， 2015， 34（21）： 1791-1803.［5］ Gong Daolin， Zhao Xutao， Guangbi， et al. Preparation and properties of isoprene-grafted styrene-butadiene rubber in latex［J］. Journal of Elastomers and Plastics， 2015， 47（6）： 539-548.［6］ 孙工， 何威. 改性丁基橡胶［J］. 橡胶科技市场， 2009， 7（19）： 19-22.［7］ 林浩， 周元林， 付万发， 等. 溴丁基胶乳乳化工艺研究［J］. 橡胶工业， 2011， 58（1）： 43-46.［8］ 张丹丹， 赵维梅， 肖代明， 等. 十二烷基苯磺酸钠表面张力的研究［J］. 辽宁化工， 2012， 41（7）： 678-679.［9］ 陈奕. 胶乳法溴化丁基橡胶的制备与表征［D］. 海口： 海南大学， 2019.［10］ 辛欣. 新型反式聚异戊二烯胶乳的制备及表征［D］. 青岛： 青岛科技大学， 2018.［11］ 李俊杰. 聚异戊二烯橡胶制备异戊胶乳的工艺研究［D］. 大连： 大连理工大学， 2018.［12］ 张雯， 袁荞龙， 吴树森. 异戊二烯橡胶的乳化与乳液稳定性研究［J］. 胶体与聚合物， 2010， 28（2）： 55-58.［13］ 刘芸， 王春芙， 段芳， 等. 稀土系聚异戊二烯胶乳乳化配方的优化［J］. 橡胶工业， 2018， 65（5）： 534-537.［14］ 刘芸. 稀土系聚异戊二烯胶乳的制备、表征及应用［D］. 青岛： 青岛科技大学， 2017.［15］ 段芳. 锂系聚异戊二烯橡胶的合成及其胶乳的制备［D］. 青岛： 青岛科技大学， 2017.［16］ 陈奕， 薛行华， 朱文靖， 等. 溴化工艺对溴化丁基橡胶溴含量及凝胶含量的影响［J］. 高分子材料科学与工程， 2018， 34（7）： 31-34.［17］ 魏邦柱. 胶乳·乳液应用技术［M］. 北京： 化学工业出版社， 2003： 113.