|本期目录/Table of Contents|

[1]庄 毅,王雷雷,郑方远,等.不同种类硫化剂对氢化丁腈橡胶性能的影响[J].合成橡胶工业,2023,1:51-54.
　ZHUANG Yi,WANG Lei-lei,ZHENG Fang-yuan,et al.Effect of different curing agents on properties of hydrogenated nitrile rubber[J].China synthetic rubber industy,2023,1:51-54.
点击复制

不同种类硫化剂对氢化丁腈橡胶性能的影响(PDF)

《合成橡胶工业》[ISSN:1000-1255/CN:62-1036/TQ]

期数:
2023年1期
页码:
51-54
栏目:
出版日期:
2023-01-15

文章信息/Info

Title:
Effect of different curing agents on properties of hydrogenated nitrile rubber
文章编号:
1000-1255（2023）01-0051-04
作者:
庄 毅1; 王雷雷2; 郑方远2; 徐 林2?鄢
1. 中国石油化工集团有限公司，北京 100728； 2. 中国石化北京化工研究院 燕山分院/橡塑新型材料合成国家工程研究中心，北京 102500
Author(s):
ZHUANG Yi1;  WANG Lei-lei2;  ZHENG Fang-yuan2;  XU Lin2
1. China Petrochemical Corporation，Beijing 100728，China; 2. Yanshan Branch of Beijing Research Institute of Chemical Industry/National Engineering Research Center for Synthesis of Novel Rubber and Plastic Materials, SINOPEC, Beijing 102500，China
关键词:
氢化丁腈橡胶; 硫化剂; 门尼黏度; 硫化特性; 物理机械性能; 耐老化性能; 耐油性能
Keywords:
hydrogenated nitrile rubber;  curing agent;  Mooney viscosity;  curing characteristics;  physical and mechanical property;  aging resistance;  oil resistance
分类号:
TQ 333.7
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2023.01.0051
文献标识码:
B
摘要:
研究了硫化剂过氧化二异丙苯（DCP）、双叔丁基过氧化异丙基苯（BIPB）和2，5-二甲基-2，5-双(叔丁基过氧化)己烷（DHBP）对氢化丁腈橡胶性能的影响。结果表明，在分解出相同自由基数量的情况下，使用DCP胶料的门尼黏度增值最小，焦烧时间最短、硫化速率最快，硫化胶的拉伸强度最小，耐老化性能最好；使用DHBP胶料的焦烧时间最长、硫化速率最慢，硫化胶的硬度和定伸应力都更低，拉伸强度和扯断伸长率均为最高，压缩永久变形和耐油性能都是最差；使用BIPB橡胶的焦烧时间、硫化速率和拉伸强度均居于前二者中间，压缩永久变形最小，耐老化性能最差，门尼黏度增值与使用DHBP相当，其他物理机械性能和耐油性能与使用DCP相当。
Abstract:
The effect of dicumyl peroxide(DCP), di-tert-butylperoxyisopropyl benzene (BIPB) and 2,5-dimethyl-2,5-di-tert-butylperoxy hexane（DHBP） on properties of hydrogenated nitrile rubber（HNBR）were investigated. The results showed that, in the case of decomposing the same number of free radicals, the compound from DCP had the lowest Mooney viscosity increment, the shortest scorch time, the fastest curing speed, the worst tensile strength and the best hot air aging resistance. The compound from DHBP had the longest scorch time, the slowest cu-ring rate, the lowest hardness and modulus, the hi-ghest tensile strength and elongation at break, the worst compression set and oil resistance. The scorch time, curing speed and tensile strength of the compound from BIPB were in the middle of the first two, with the minimum compression set and worst hot air aging resistance, the Mooney viscosity increment was equivalent to that from DHBP, and other physical and mechanical properties and oil resistance were equivalent to that from DCP.