 ZHANG Wen-jing,GAO Wen-ke,LIU Jin-hui,et al.Preparation and properties of carboxyl-modified 1,2-polybutadiene with widely adjustable functionality[J].China synthetic rubber industy,2022,6:516.
点击复制

官能度宽域可调的羧基改性1,2-聚丁二烯的制备及性能(PDF)

《合成橡胶工业》[ISSN:1000-1255/CN:62-1036/TQ]

期数:
2022年6期
页码:
516
栏目:
出版日期:
2022-11-15

文章信息/Info

Title:
Preparation and properties of carboxyl-modified 1,2-polybutadiene with widely adjustable functionality
文章编号:
DOI:10.19908/j.cnki.ISSN1000-1255.2022.06.0516
作者:
张文静高文珂刘金慧华 静耿洁婷
青岛科技大学 橡塑材料与工程教育部重点实验室/山东省橡塑材料与工程重点实验室,山东 青岛 266042
Author(s):
ZHANG Wen-jing GAO Wen-ke LIU Jin-hui HUA Jing GENG Jie-ting*
Key Laboratory of Rubber-Plastics of Ministry of Education/Shandong Provincial Key Laboratory of Rubber and Plastics, Qingdao University of Science and Technology, Qingdao 266042, China
关键词:
12-聚丁二烯巯基-烯点击化学官能度阻尼温域
Keywords:
-
分类号:
-
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2022.06.0516
文献标识码:
-
摘要:
采用室温光引发巯基-烯点击化学法制备羧基功能化1,2-聚丁二烯(1,2-PB)。结果表明,3-巯基丙酸成功接枝到1,2-PB上,羧基官能度在0~46.2%宽域内可调。通过调节分子链上羧基含量可控制氢键的作用强度,使得聚合物的玻璃化转变温度从-2.1 ℃提高到26.3 ℃,未加填料增强的橡胶的拉伸强度可达15.5 MPa,扯断伸长率均大于350%;材料的有效阻尼温域从-8.28-3.83 ℃拓宽至23.63-73.03 ℃;1,2-PB/COOH中高的羧基接枝率赋予材料优异的金属黏附性能,分子链中剩余双键还可与丁苯橡胶基体共硫化,使其与橡胶层具有优异的黏附性能。
Abstract:
-