Title:
Preparation and properties of super hydrophilic material based on ethylene-vinyl acetate copolymer/nitrile rubber thermoplastic vulcanizate
文章编号:
1000-1255（2022）06-0500-05
作者:
张卫然; 奉若涛; 杨林基; 王兆波*
青岛科技大学 材料科学与工程学院, 山东 青岛 266042
Author(s):
ZHANG Wei-ran;  FENG Ruo-tao;  YANG Lin-ji;  WANG Zhao-bo
College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
关键词:
动态硫化; 丁腈橡胶; 乙烯-乙酸乙烯酯共聚物; 超亲水性能; 模板法; 热塑性硫化橡胶
Keywords:
dynamic vulcanization;  nitrile rubber;  ethylene-vinyl acetate copolymer;  super hydrophilicity;  template method;  thermoplastic vulcanizate
分类号:
TQ 333.7
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2022.06.0500
文献标识码:
B
摘要:
采用动态硫化法制备了基于乙烯–乙酸乙烯酯共聚物/丁腈橡胶的热塑性硫化橡胶（EVA/NBR TPV），以不同型号金相砂纸为模板，通过模压法在其表面构建具有微纳米结构的表面，研究了橡塑质量比对EVA/NBR TPV粗糙表面超亲水行为的影响及EVA/NBR TPV超亲水表面的微观结构和超亲水性能，并初步探讨了EVA/NBR TPV表面的亲水机制。结果表明，当EVA/NBR TPV的橡塑质量比为20/80时，采用模板法且以耐水砂纸为模板制得的EVA/NBR TPV表面亲水性较好。其中，当橡塑质量比为20/80时，以NO 1000砂纸为模板，模压温度为165 ℃，经过预热10 min、热压3 min、冷压5 min后制得的EVA/NER TPV薄膜表面的亲水性最佳。
Abstract:
Thermoplastic vulcanizate based on ethylene-vinyl acetate copolymer/nitrile rubber (EVA/NBR TPV) was prepared by dynamic vulca-nization method, the effect of the mass ratio of rubber to plastic on the superhydrophilic behavior of EVA/NBR TPV surface was researched, the microstructure and super hydrophilicity of EVA/NBR TPV super hydrophilic surface were studied, and the hydrophilic mechanism was preliminarily discussed. The results showed that the surface hydrophilicity of EVA/NBR TPV prepared by template method with water-resistant sandpaper as template was better when the mass ratio of rubber to plastic of EVA/NBR TPV was 20/80. The surface hydrophilicity of EVA/NBR TPV film with the mass ratio of rubber to plastic of 20/80 was the best when the sandpaper NO 1000 was used as the template at 165 °C after being preheated for 10 min, being hot pressed for 3 min and being cold-pressed for 5 min.

参考文献/References

［1］ 董青. 表面润湿性对粗糙表面接触界面摩擦特性的影响［D］. 合肥： 合肥工业大学, 2016.［2］ 宋金龙, 陆遥, 黄帅, 等. 极端润湿性表面研究与应用进展［J］. 科技导报, 2015, 33（15）： 92-100.［3］ Dey A, Chandrabose G, Ghosh P, et al. Atmospheric pressure plasma engineered superhydrophilic CuO surfaces with enhanced catalytic activities［J］. Applied Surface Science, 2021, 564： 150413.［4］ Wang Rong, Hashimoto Kazuhito, Fujishima Akira, et al. Light-induced amphiphilic surfaces［J］. Nature, 1997, 388（6641）： 431-432.［5］ 孙琳. 杂化TiO2多孔薄膜及其无紫外光辐照下的超亲水特性［D］. 杭州： 浙江大学, 2014.［6］ 蔡东宝. 自清洁涂层制备工艺的研究与应用［D］. 西安： 西安建筑科技大学, 2018.［7］ 刘靖, 王威, 余新泉, 等. 超亲水防雾表面研究进展［J］. 表面技术, 2020, 49（12）： 75-92.［8］ 刘昌泉, 徐进良, 纪献兵. 超亲水/超疏水匹配超薄热管的传热特性［J］. 化工进展, 2018, 37（6）： 2067-2076.［9］ 韩天元. 生物粘附启发多功能亲水涂层的制备及其性能研究［D］. 长春： 吉林大学, 2021.［10］ 蔡安江, 闫雪蕊, 叶向东. 自清洁、防雾聚氨酯-SiO2复合超亲水透明涂层的制备与表征［J］. 复合材料学报, 2020, 37（1）： 191-197.［11］ 张鹏. 超浸润表面在油水分离中的应用［J］. 石油化工应用, 2021, 40（10）： 13-18.［12］ 徐弘. 溶胶-凝胶法制备SiO2超亲水涂层的研究［D］. 哈尔滨： 哈尔滨工业大学, 2019.［13］ 梁涛. 有机及有机/无机杂化超亲水涂层的制备、性能及应用［D］. 广州： 华南理工大学, 2017.［14］ 王强, 白洁, 朱嘉琦. 超浸润金刚石薄膜的研究进展［J］. 表面技术, 2020, 49（6）： 1-9.［15］ 赵潇. 超亲水涤纶织物和聚偏氟乙烯多孔膜的制备与应用研究［D］. 广州：华南理工大学, 2020.［16］ 常忠帅. 超亲水-水下超疏油有机-无机复合网膜的构筑及其油水分离性能的研究［D］. 镇江： 江苏大学, 2018.［17］ 蒋志成, 王君豪, 王稳启, 王兆波. 基于高密度聚乙烯/丁苯橡胶热塑性硫化胶的超疏水/超亲油油水分离膜的制备及性能［J］. 合成橡胶工业, 2021, 44（6）： 462-467.［18］ Quéré D. Wetting and Roughness［J］. Annual Review of Materials Research, 2008, 38： 71-99.

备注/Memo

备注/Memo:
山东省自然科学基金资助项目（ZR 2021 ME 028）；2021年山东省大学生创新创业训练计划项目（S 202110426032）。
更新日期/Last Update: 2022-11-15