Title:

Radiation cross-linking technology and co-vulcanization of natural rubber/ethylene-propylene diene monomer blends

文章编号:

1000-1255（2023）03-0210-05

作者:

程安仁1; 2; 陆永俊1?鄢; 矫 阳1; 郭月莹1

1. 北京市科学技术研究院 北京市射线应用研究中心有限公司/辐射新材料北京市重点实验室，北京 100015；2. 兴原认证中心有限公司，北京 100085

Author(s):

CHENG An-ren1; 2;  LU Yong-jun1;  JIAO Yang1;  GUO Yue-ying1

1. Beijing Research Centre for Radiation Application Co Ltd/Beijing Key Laboratory of Radiation Advanced Materials, Beijing 100015, China; 2. Xingyuan Certification Center Co Ltd, Beijing 100085, China

关键词:

天然橡胶; 三元乙丙橡胶; 共混胶; 共硫化; 热硫化; 辐射交联; 力学性能

Keywords:

natural rubber;  ethylene-propylene diene monomer;  blend;  co-vulcanization;  heat-vulcanization;  radiation cross-linking;  mechanical pro-perty

分类号:

TQ 330.1＋3

DOI:

DOI:10.19908/j.cnki.ISSN1000-1255.2023.03.0210

文献标识码:

B

摘要:

制备了具有不同共混比的天然橡胶（NR）/三元乙丙橡胶（EPDM）共混胶，对NR/EPDM热硫化胶进行应力-应变测试，筛选出热硫化过程中共硫化问题最严重的共混胶，采用辐照交联技术对其进行不同辐射吸收剂量的辐射处理，优选出最佳辐射吸收剂量；在最佳辐射吸收剂量下将不同共混比的NR/EPDM热硫化胶进行辐射处理，并对辐射处理前后共混胶的性能进行对比分析。结果表明，当NR和EPDM的质量比为40/60时NR/EPDM热硫化胶的综合力学性能最差；当辐射吸收剂量为100 kGy时，NR/EPDM共混胶的综合性能最佳，经辐射处理后不同共混比NR/EPDM共混胶的100%定伸应力均得到提高且提升幅度无显著差别；不同共混比NR/EPDM的共混胶经辐射处理后的拉伸强度和扯断伸长率曲线均由辐射处理前的类“U形”变为近似直线；辐射处理后NR/EPDM共混胶的扯断伸长率均下降，EPDM相的扯断伸长率下降幅度比NR相大。

Abstract:

Natural rubber (NR)/ethylene-propylene-diene rubber (EPDM) blends with different blending ratios were prepared, the heat-vulcanized NR/EPDM vulcaniztes were analyzed by the stress-strain test, the blend with the most serious co-vulcanization problem in the process of heat-vulcanization was selected for radiation processing with diffe-rent radiation absorption dose by radiation cross-linking technology, and the optimal radiation absorption dose was preferred. Radiation treatment of the heat-vulcanized NR/EPDM vulcaniztes with different blending ratios was carried out with the optimal absorption dose, and the properties of the heat-vulcanized NR/EPDM vulcaniztes before and after radiation treatment were compared. The results showed that the comprehensive mechanical properties of the heat-vulcanized NR/EPDM vulcanizte were the worst when the mass ratio of NR to EPDM was 40/60; when the radiation absorption dose was 100 kGy, the comprehensive mechanical properties of NR/EPDM blends were the best, and modulus at 100% of NR/EPDM blends with different blending ratios all increased and there was no significant difference in the magnitude of the increase in modulus at 100% of NR/EPDM blends with different blending ratios after radiation treatment; the curves of tensile strength and elongation at break of NR/EPDM blends with different blending ratios all changed from the “U-shaped” before radiation treatment to the approximate linear after radiation treatment; after radiation treatment elongation at break of NR/EPDM blends all decreased and the magnitudes of the increase in elongation at break of EPDM phase were larger than those of NR phase in NR/EPDM blends.

参考文献/References

［1］ 游长江. 橡胶并用与橡塑共混［M］. 北京： 化学工业出版社， 2014： 40-110.［2］ 熊金平. 现代橡胶选用设计［M］．北京： 化学工业出版社， 2014： 14-139.［3］ 赵术英， 纪金权. NR/EPDM并用胶性能研究［J］. 中国橡胶， 2020， 36（11）： 55-58.［4］ 江羿锋. 天然橡胶/三元乙丙橡胶并用胶性能及改进研究［J］. 当代化工研究， 2018（2）：78-79.［5］ 保罗 D R， 巴克纳尔 C B. 聚合物共混物： 组成与性能［M］. 北京： 科学出版社， 2004： 798-802.［6］ 时佰文， 高洪强， 肖建斌. NR/EPDM共混胶的制备与性能研究［J］. 弹性体， 2017， 27（1）： 46-49.［7］ 程安仁， 矫阳， 陆永俊， 等. 天然橡胶/三元乙丙橡胶并用胶共混改性研究进展［J］. 合成橡胶工业, 2022， 45（3）： 259-267.［8］ 冯芝娟. NR/EPDM共混材料的制备与性能研究［D］. 青岛： 青岛科技大学， 2015.［9］ 钱坤. NR/EPDM合金弹性体的制备及其耐热老化性能研究［D］. 合肥： 安徽大学， 2020.［10］ 黄必弟， 林升博, 钟帅， 等.汽车用NR/EPDM雨刮胶料的研究［J］. 广东化工, 2020， 47（7）： 50-51.［11］ Ghosh A K， Basu D K. Effect of diisopropyl thiophosphoryl-N-oxydiethylene sulfenamide and some disulfidic compounds in the covulcanization of NR-EPDM blends［J］. Polymer International, 2003， 52（8）： 1370-1381．［12］ 程安仁， 张艳霞， 汪文昭， 等. 天然橡胶辐射预硫化技术的应用研究［J］. 特种橡胶制品， 2016， 37（3）： 45-48.［13］ 赵雪娜， 程安仁， 张艳霞等. γ射线辐照对三元乙丙橡胶动态力学性能的影响［J］. 橡胶科技, 2017， 15（10）： 15-17.［14］ 赵文彦， 潘秀苗. 辐射加工技术及其应用［M］. 北京： 兵器工业出版社， 2003： 4-9.［15］ 米爱军， 王炳衡， 程安仁， 等. 一种天然橡胶与三元乙丙橡胶的共混橡胶： 中国， 202111360559.1［P］. 2022-03-08.