Title:

Effects of Mooney viscosity and mass fraction of bound acrylonitrile on mechanical properties and degree of swelling of nitrile rubber 3604 and 2707

文章编号:

1000-1255（2023）03-0199-05

作者:

张守汉; 肖 晔; 李铁柱

中国石油 兰州石化公司，甘肃 兰州 730060

Author(s):

ZHANG Shou-han; XIAO Ye; LI Tie-zhu

Lanzhou Petrochemical Company, PetroChina, Lanzhou 730060, China

关键词:

丁腈橡胶; 生胶; 硫化胶; 门尼黏度; 结合丙烯腈质量分数; 拉伸强度; 扯断伸长率; 溶胀度

Keywords:

nitrile rubber;  raw rubber;  vulca-nizate;  Mooney viscosity;  mass fraction of bound acrylonitrile;  tensile strength;  elongation at break;  degree of swelling

分类号:

TQ 333.6

DOI:

DOI:10.19908/j.cnki.ISSN1000-1255.2023.03.0199

文献标识码:

A

摘要:

研究了丁腈橡胶（NBR）3604和2707生胶门尼黏度和结合丙烯腈质量分数对硫化胶的拉伸强度、扯断伸长率及溶胀度的影响。结果表明，随着生胶门尼黏度的增加，NBR 3604和NBR 2707硫化胶的拉伸强度和扯断伸长率均呈线性增加的趋势，而溶胀度则均呈线性减小的趋势；NBR 3604和NBR 2707生胶门尼黏度每增加1个单位，硫化胶的拉伸强度分别增加0.15 MPa和0.02 MPa，扯断伸长率分别增加1.13%和1.30%，溶胀度分别减小0.02%和0.21%。随着结合丙烯腈质量分数的增加，NBR 3604和NBR 2707硫化胶的拉伸强度均呈线性增大的趋势，而扯断伸长率和溶胀度则均呈线性减小的趋势；NBR 3604和NBR 2707结合丙烯腈质量分数每增加1%，硫化胶的拉伸强度均增加0.04 MPa，扯断伸长率分别减小0.08%和2.77%，溶胀度分别减小0.06%和0.25%。

Abstract:

The effects of Mooney viscosity (MV) of raw rubbers and mass fraction of bound acrylonitrile (wAN) of nitrile rubber (NBR) 3604 and NBR 2707 on tensile strength (Ts), elongation at break (Eb) and degree of swelling (Ds) of the vulcanizates were studied. The results showed that with the increase in MV of raw rubbers, Ts and Eb of NBR 3604 and NBR 2707 vulcanizates all showed a linear increasing trend, whereas their Ds all showed a linear decreasing trend; when MV of raw rubbers of NBR 3604 and NBR 2707 increased by 1 unit, Ts of their vulca-nizates increased by 0.15 MPa and 0.02 MPa respectively, Eb of their vulcanizates increased by 1.13% and 1.30% respectively, and Ds of their vulcanizates decreased by 0.02% and 0.21% respectively. With the increase in wAN, Ts of NBR 3604 and NBR 2707 vulcanizates all showed a linear increasing trend, whereas Eb and Ds of their vulcanizates all showed a linear decreasing trend; when wAN of NBR 3604 and NBR 2707 increased by 1%, Ts of their vulcanizates all increased by 0.04 MPa, Eb of their vulcanizates decreased by 0.08% and 2.77% respectively, and Ds of their vulcanizates decreased by 0.06% and 0.25% respectively.

参考文献/References

［1］ 张传贤， 火金三， 于奎， 等. 丁腈橡胶［M］. 北京： 中国石化出版社， 2010： 1.［2］ 赵旭涛， 刘大华. 合成橡胶工业手册［M］. 北京： 化学工业出版社， 2011： 356.［3］ 王艳秋. 橡胶塑炼与混炼［M］. 北京： 化学工业出版社， 2006： 116.［4］ 翁国文. 橡胶硫化［M］. 北京： 化学工业出版社， 2005： 17-19.［5］ 张守汉， 应婵娟， 马莉莉. 门尼黏度对丁腈橡胶拉伸性能的影响［J］. 弹性体， 2019， 29（5）： 26-28.［6］ 张守汉， 郑彩琴， 马莉莉， 等. 不同硫化时间下丁腈橡胶结合丙烯腈含量与拉伸性能的关系［J］. 弹性体， 2020， 30（3）： 25-29.［7］ 张守汉， 郑彩琴， 马莉莉， 等. 自然环境中抗氧剂含量对丁腈橡胶拉伸性能的影响［J］. 弹性体， 2020， 30（5）： 22-25.［8］ 陈玉祥， 侯铎， 王霞. 添加剂对丁腈橡胶结构和性能的影响［J］. 弹性体， 2008， 18（3）： 61-64.［9］ 陈云萍， 王炳昕， 刘莉， 等. 微观结构对丁腈橡胶硫化胶物理性能的影响［J］. 橡胶工业， 2013， 60（4）： 226-229.［10］ 陈昊诚， 董瑞宝， 王文玉， 等. 丁腈橡胶序列结构对其硫化速率及力学性能的影响［J］. 高分子材料科学与工程， 2019， 35（7）： 9-12.［11］ 张宝岗. 丁腈橡胶微观结构与性能及高性能磁性丁腈橡胶的制备研究［D］. 青岛： 青岛科技大学， 2013.［12］ 王春龙， 孙丽君， 吴毅， 等. SH/T 1159—2010丙烯腈-丁二烯橡胶（NBR）溶胀度的测定［S］. 北京： 中国石化出版社， 2011： 1-6.［13］ 何曼君， 陈维孝， 董西侠. 高分子物理［M］. 上海： 复旦大学出版社， 1990： 312-314.