Title:
Regulation of bound acrylonitrile content of nitrile rubber with low acrylonitrile content
文章编号:
1000-1255（2023）03-0193-06
作者:
胡育林; 王永峰; 钟启林?鄢; 赵志超; 邵 卫
中国石油石油化工研究院 兰州化工研究中心/甘肃省合成橡胶工程技术研究中心/中国石油和化学工业联合会合成橡胶工程研究中心，兰州 730060
Author(s):
HU Yu-lin;  WANG Yong-feng;  ZHONG Qi-lin;  ZHAO Zhi-chao;  SHAO Wei
Lanzhou Petrochemical Research Center, Petrochemical Research Institute, PetroChina/Synthetic Rubber Engineering Technology Research Center of Gansu/Petroleum and Chemical Industry Federation Synthetic Rubber Engineering Research Center of China, Lanzhou 730060, China
关键词:
丁腈橡胶; 结合丙烯腈含量; 单体竞聚率; 单体转化率; 单体配比
Keywords:
nitrile rubber;  bound acrylonitrile content;  monomer reactivity ratio ;  monomer conversion;  monomer ratio
分类号:
TQ 333.6
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2023.03.0193
文献标识码:
A
摘要:
考察了聚合反应过程中NBR产品中结合丙烯腈含量的影响因素，主要包括单体竟聚率、单体转化率、单体浓度、聚合反应温度和压力，分析了产品的结构组成，并进行了聚合反应动力学探究和重复性试验。结果表明，在聚合反应温度为5.0 ℃、聚合压力为0.15～0.20 MPa条件下，采用多段补加丙烯腈的方式，同时将单体转化率控制在70%～75%，可得到丙烯腈结构单元分布均匀、结合丙烯腈质量分数为17%～19%的NBR产品，所用聚合配方和工艺具有良好的重复性。
Abstract:
The factors affecting the bound acrylonitrile content of NBR product during the polyme-rization process were investigated, including monomer reactivity ratio, monomer conversion, monomer concentration, and polymerization temperature and pressure, the structural composition of the product was analyzed, and the polymerization reaction kinetics and repeatability experiment were carried out. The results showed that under the polymerization temperature of 5.0 ℃ and polymerization pressure of 0.15-0.20 MPa, NBR products with uniform distribution of acrylonitrile structure units and mass fraction of bound acrylonitrile of 17%-19% could be obtained by using multi-stage addition of acrylonitrile and controlling the monomer conversion of 70%-75%. The polymerization formula and process had good repeatability.

参考文献/References

［1］ 李波， 赵洪国， 吴宇等. 兰州石化丁腈橡胶产品及应用［J］. 当代石油石化. 2013， 21（12）： 30-35.［2］ 钟启林， 张志强， 高志兴， 等. 低腈含量丁腈橡胶的中试放大［J］. 合成橡胶工业， 2014， 37（3）： 165-168.［3］ 丁攀攀， 贾连辉， 王静， 等. 耐高温丁腈橡胶及其应用以及密封橡胶制品的无痕分段硫化方法和主驱动密封圈： 中国， 113637244 A［P］. 2021-11-12.［4］ 汤致华. 丁腈橡胶密封材料的低温特性［J］. 内燃机与配件， 2020（4）： 220-221.［5］ 赵旭涛， 刘大华. 合成橡胶工业［M］. 2版. 北京： 化学工业出版社， 2006： 709-722.［6］ 王兴刚， 齐永新， 彭仁苹， 等. 国丁腈橡胶产业发展现状及未来发展趋势［J］. 高分子通报， 2016， 29（4）： 1-16.［7］ 李波， 赵洪国， 吴宇， 等. 兰州石化丁腈橡胶产品及应用［J］. 当代石油石化， 2013， 21（12）： 30-34.［8］ 张传贤， 火金三， 于奎， 等. 丁腈橡胶［M］. 北京： 中国石化出版社， 2010： 51-54.［9］ 潘祖仁. 高分子化学［M］. 北京： 化学工业出版社， 2007： 126-128.［10］ 桂强， 梁琨， 钟启林， 等 无皂乳液聚合制备丁二烯-丙烯腈橡胶［J］. 弹性体， 2011， 21（5）： 40-43.