天然橡胶硫化胶耐臭氧老化性能的快速评价方法

《合成橡胶工业》[ISSN:1000-1255/CN:62-1036/TQ]

期数:
2023年2期
页码:
134-138
栏目:
加工 · 应用
出版日期:
2023-03-15

文章信息/Info

Title:
Quick evaluation method of ozone aging resistance for natural rubber vulcanizate
文章编号:
1000-1255（2023）02-0134-05
作者:
吴玲玲; 穆洪帅; 肖同亮; 谭莲影; 余海文; 黄良平; 王雪飞
株洲时代新材料科技股份有限公司 轨道交通事业部，湖南 株洲 412007
Author(s):
WU Ling-ling;  MU Hong-shuai;  XIAO Tong-liang;  TAN Lian-ying;  YU Hai-wen;  HUANG Liang-ping;  WANG Xue-fei
Rail Transportation Business Unit, Zhuzhou Times New Material Technology Co Ltd, Zhuzhou 412007, China
关键词:
天然橡胶; 硫化胶; 耐臭氧老化性能; 防护蜡; 伸长率; 臭氧浓度; 相对湿度
Keywords:
natural rubber;  vulcanizate;  ozone aging resistance;  protective wax;  elongation;  ozone concentration;  relative humidity
分类号:
TQ 330.7
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2023.02.0134
文献标识码:
B
摘要:
考察了伸长率、臭氧体积分数、相对湿度等试验条件对天然橡胶（NR）硫化胶耐静态臭氧老化性能的影响，建立了NR硫化胶耐臭氧老化的快速评价方法，并用该方法优选出了适宜NR胶料的防护蜡及其适宜用量。结果表明，提高伸长率，增加臭氧体积浓度和相对湿度，试样表面开始出现臭氧龟裂且龟裂程度逐渐增大。炭黑填充的NR硫化胶耐臭氧老化性能适宜的快速评价条件为：温度为40 ℃、伸长率为50%、臭氧体积分数为1.00×10-4%、相对湿度为50%。提高防护蜡中异构烷烃含量和中间碳数烷烃含量以及防护蜡用量，有利于改善NR硫化胶耐臭氧老化性能。运用该快速评价方法筛选出NR硫化胶耐臭氧老化性能较好的为防护蜡A，其最佳用量为3份。
Abstract:
The effects of elongation, ozone volume concentration, relative humidiy on ozone aging resistance of natural rubber (NR) vulcanizates had been investigated. A quick evaluation method of ozone aging resistance for NR vulcanizate was established. The appropriate type and amount of protective wax for NR vulcanizate were optimized by this method. Test results showed that the ozone cracking began to appear on the surface of samples and the degree of cracking gradually increased with higher elogation and ozone volume concentration as well as relative humidity. The test condition of 50% maximum elongation and 1.00×10-4% ozone volume fraction with 50% relative humidity at 40 ℃ could characterize the resistance to ozone aging of NR vulcanizates filled with carbon black quickly. The protective wax with high content of non-normal pafaffins and intermediate carbon paraffins had good protection effect of static ozone for NR vulcanizates. Using this quick evaluation method, protective wax A was found to have better performance of ozone aging resistance for NR vulcanizate. And the optimum amount of protective wax A was 3 phr.

参考文献/References

［1］ 杨清芝， 现代橡胶工艺学［M］. 北京：中国石化出版社，2014：313-322. ［2］ 王梦蛟，龚怀耀，薛广智，等. 橡胶工业手册：配合剂［M］. 北京：化学工业出版社，1989：250-251. ［3］ 中国化工学会橡胶专业委员会. 橡胶助剂手册：配合剂［M］. 北京：化学工业出版社，2000：291-293. ［4］ 王作龄. 最新橡胶工艺原理（十三）［J］. 世界橡胶工业，2004，31（4）：49-56. ［5］ 黄文捷，黄雨林. 高分子材料老化试验方法简介［J］. 汽车零部件，2009，2（9）：71-74. ［6］ 李代强，冯萍. 提高全钢工程机械子午线轮胎侧胶和胎圈外护胶耐臭氧老化性能的研究［J］. 橡胶科技市场，2009，3（11）：17-21. ［7］ 张晓芳，王玲玲，邓涛. 不同温度下橡胶防护蜡抗臭氧老化性能的研究［J］. 特种橡胶制品，2015，36（6）：41-45. ［8］ 苏小平，李伟，刘楠. 快速喷出耐臭氧保护膜天然橡胶胶料的研制［J］. 特种橡胶制品，2016，37（3）：33-36. ［9］ 马德龙，孙庆刚，赵红霞，等. 轮胎胎侧胶的耐老化性能及喷霜变色问题研究［J］. 橡胶科技，2021，19（5）：223-228. ［10］ 陈长生. 橡胶制品臭氧老化的物理防护方法［J］. 制品，1997，1（1）：21-25. ［11］ 武爱军. 下一代汽车与高分子材料［J］. 世界橡胶工业，2013，40（10）：47-50. ［12］ 高天奇，王兆波. 轿车轮胎耐臭氧老化性能研究［J］. 青岛科技大学学报（自然科学版），2018，39（1）：88-91. ［13］ 孙艳妮，何宁，孙钦军，等. 轮胎动态臭氧老化性能的研究［J］. 青岛科技大学学报（自然科学版），2019，40（4）：91-97.