Title:
Synthesis of polar link-branched polybutadiene based on click chemistry and reversible addition-fragmentation chain transfer radical polymerization
文章编号:
1000-1255（2023）01-0002-04
作者:
赵姜维1; 石 艳2; 李建成1; 邵明波1; 徐 林1
1． 中国石化北京化工研究院 燕山分院/橡塑新型材料合成国家工程研究中心，北京 102500； 2． 北京化工大学 材料科学与工程学院，北京 100029
Author(s):
ZHAO Jiang-wei1;  SHI Yan2;  LI Jian-cheng1;  SHAO Ming-bo1;  XU Lin1
1. National Engineering Research Center for Synthesis of Novel Rubber and Plastic Materials/ Yanshan Branch of Beijing Research Institute of Chemical Industry, SINOPEC, Beijing 102500, China; 2. College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China
关键词:
聚丁二烯; 点击化学; 可逆加成-断裂链转移自由基聚合; 接枝
Keywords:
polybutadiene;  click chemistry;  reversible addition-fragmentation chain transfer radical polymerization;  graft
分类号:
TQ 333.2
DOI:
DOI:10.19908/j.cnki.ISSN1000-1255.2023.01.0002
文献标识码:
B
摘要:
以1-硫代甘油作为改性剂、聚丁二烯为主链，通过热引发和光引发合成了侧基含有羟基的聚丁二烯，以S-1-十二烷基-S′（α-α′-二甲基-α′′乙酸）-三硫代碳酸酯作为可逆加成-断裂链转移自由基聚合试剂、偶氮二异丁腈为引发剂，合成了端羧基聚N，N-二甲基丙烯酰胺，然后将两种官能化的聚合物进行酯化反应制得聚N，N-二甲基丙烯酰胺接枝聚丁二烯。结果表明，采用光引发可以显著提高点击化学的反应效率。用核磁共振氢谱证实了产物含羟基聚丁二烯和端羧基聚N，N-二甲基丙烯酰胺以及接枝聚合物的结构，并显示通过这种方法所制备接枝聚合物的接枝链数目和长度均可控。
Abstract:
Polybutadiene containing hydroxyl group was synthesized by thermal initiation and photoinitiation using 1-thioglycerol as modifier and polybutadiene as main chain. Carboxyl-terminated poly (N,N-dimethyl acrylamide) was synthesized with S-1-dodecyl-S′(α-α′-dimethyl-α"acetic acid)-trithiocarbonate as reversible addition-fragmentation chain transfer radical polymerization reagent and azo-diisobutyronitrile as initiator. Then the two functiona-lized polymers were esterified to prepare polybuta-diene grafted with N,N-dimethylacrylamide. The results showed that the efficiency of click chemical reaction could be significantly improved by using photoinitiation. The structure of hydroxy-containing polybutadiene and carboxy-terminated poly(N,N-dimethylacrylamide) as well as grafted polymers were confirmed by hydrogen spectrum of nuclear magnetic resonance, and the number and length of grafted polymers prepared by this method were controllable.

参考文献/References

［1］ 谭捷， 侯姝婧， 李佳源， 等. 我国聚丁二烯橡胶生产技术进展及市场分析［J］. 弹性体， 2021， 31（1）： 77-82.［2］ 赵姜维， 李传清， 张杰， 等. 稀土系橡胶国内外生产现状及发展趋势［J］. 中国橡胶， 2012， 28（5）： 16-19.［3］ 廖禄生. 采用ATRP合成结构可控的天然橡胶接枝共聚物［D］. 海口： 海南大学， 2013.［4］ Zhang Z Y， Wang J C， Tu Q， et al. Surface modification of PDMS by surface-initiated atom transfer radical polymerization of water-soluble dendronized PEG methacrylate［J］. Colloids and Surfaces （B）： Biointerfaces， 2011， 88（1）： 85-92.［5］ 郗向丽. 乙丙橡胶接枝聚合物的制备［D］. 北京： 北京化工大学， 2007.［6］ 杨耀华， 廖建和， 廖禄生， 等. 采用ATRP合成天然橡胶接枝共聚物（Ⅱ）：ENR-g-PS的制备［J］. 合成化学， 2012， 20（2）： 169-173.［7］ 刘清， 张秋禹， 陈少杰， 等. 巯基-烯/炔点击化学研究进展［J］. 有机化学， 2012， 32（10）： 1846-1863.［8］ Devaraj N K， Finn M G. Introduction： Click chemistry［J］. Chemical Reviews， 2021， 121（12）： 6697-6698.［9］ 李建成， 王雪， 赵姜维， 等. 低顺式聚丁二烯橡胶及其制备方法和HIPS树脂及其制备方法和ABS树脂： 中国， 109503746 A［P］. 2019-03-22.