Title:

Preparation and properties of nitrile rubber modified by fluorine-containing monomer

文章编号:

1000-1255（2022）05-0357-04

作者:

桂 强1; 刘 鹏2; 钟启林1; 赵志超1; 张元寿1; 张志强1

1. 中国石油石油化工研究院 兰州化工研究中心/甘肃省合成橡胶工程技术研究中心/中国石油和化学工业联合会合成橡胶工程研究中心， 兰州 730060； 2. 兰州大学 化学化工学院， 兰州 730000

Author(s):

GUI Qiang1;  LIU Peng2;  ZHONG Qi-lin1;  ZHAO Zhi-chao1;  ZHANG Yuan-shou1;  ZHANG Zhi-qiang1

1.Lanzhou Petrochemical Research Center／Synthetic Rubber Engineering Technology Research Center of Gansu Province／Synthetic Rubber Engineering Research Center of China Petroleum and Chemical Industry Federation, Petrochemical Research Institute, PetroChina, Lanzhou 730060, China; 2. School of Chemistry and Chemical Engineering, Lanzhou University, Lanzhou 730000, China

关键词:

含氟单体; 改性丁腈橡胶; 反应型偶联剂; 乳液聚合; 力学性能; 耐热空气老化性能

Keywords:

fluorine-containing monomer;  modified nitrile rubber;  reactive coupling agent;  emulsion polymerization;  mechanical property;  hot air aging resistance

分类号:

TQ 333.7

DOI:

DOI:10.19908/j.cnki.ISSN1000-1255.2022.05.0357

文献标识码:

A

摘要:

采用含氟单体甲基丙烯酸六氟丁酯、丁二烯、丙烯腈与反应型偶联剂直接进行乳液共聚制备含氟单体改性丁腈橡胶，考察了反应型偶联剂的种类及用量对聚合产物结构及性能的影响。结果表明，反应型偶联剂Q 2可与丁二烯、丙烯腈、含氟单体进行四元共聚，当含氟单体甲基丙烯酸六氟丁酯与偶联剂Q 2的质量比为1.50/1.50时，含氟单体改性丁腈橡胶的综合性能较佳，拉伸强度达到25.5 MPa，扯断伸长率为377%，耐热空气老化性能较好。

Abstract:

Nitrile rubber modified by fluorine-containing monomer was prepared by emulsion copolymerization of hexafluorobutyl methacrylate, butadiene and acrylonitrile with reactive coupling agent. And the effects of types and amount of reactive coupling agents on the structure and properties of the polymerization products were investigated. The results showed that the reactive coupling agent Q 2 could be copolymerized with butadiene, acrylonitrile and fluorine-containing monomers. When the mass ratio of hexafluorobutyl methacrylate and coupling agent Q 2 was 1.50/1.50, the comprehensive properties of nitrile rubber modified by fluorine-containing monomer were better, the tensile strength reached 25.5 MPa, the elongation at break was 377%, and the hot air aging resistance was better.

参考文献/References

［1］ 孙建英，卿凤翎. 高性能有机氟材料制备科学及应用进展［J］. 化工进展，2020，39（9）：3395-3402.［2］ Pei Mingliang， Pan Changou， Liu Peng. Facile Fabrication of superhydrophobic surface with palygorskite-poly ［2-（perfluorohexyl）ethyl methacrylate］ composite microgels［J］. Composites Communications，2021，25：100740.［3］ Long Cai， Qing Yongquan， An Kai，et al. Functional fluorination agents for opposite extreme wettability coatings with robustness， water splash inhibition， and controllable oil transport［J］. Chemical Engineering Journal，2021，415：128895.［4］ Zheng Hongpeng， Liu Li， Meng Fandi， et al. Multifunctional superhydrophobic coatings fabricated from basalt scales on a fluorocarbon coating base［J］. Journal of Materials Science & Technology，2021，84：86-96.［5］ 张永明，李虹，张恒. 含氟功能材料［M］. 北京：化学工业出版社，2008：1-4.［6］ 刘舒巍，李红飞，舒斌，等. 氟塑料的改性及其在换热器领域的应用研究进展［J］. 化工管理，2019（13）：103-104.［7］ 张传贤，火金三. 合成橡胶技术丛书——丁腈橡胶［M］. 北京：中国石化出版社，2010：149-153.［8］ Améduri B，Boutevin B，Kostov G. Fluoroelastomers： Synthesis， properties and applications［J］. Progress in Polymer Science，2001，26（1）：105-187. ［9］ Jiang Xiujuan， Xu Chuanhui， Wang Yanpeng， et al. Polyvinylidene fluoride/acrylonitrile butadiene rubber blends prepared via dynamic vulcanization［J］. Journa Macromolecular Science（Part B）： Physics， 2015，54（1）：58-70.［10］ 李庄. 氟橡胶/丁腈橡胶共混体系性能研究［J］. 世界橡胶工业，2013，40（2）：19-21.［11］ 陈竞哲，王建海，张潇，等. 氢化丁腈橡胶/氟橡胶复合材料的相容性、力学性能及热氧老化性能［J］. 合成橡胶工业，2018，41（4）：261-265.［12］ 曾斌，党海军，李辉，等. 红外光谱法研究XeF2表面氟化丁腈橡胶动力学［J］. 光谱实验室，2007，24（2）：255-260.［13］ Zhu Zhongmeng， Xia Yan， Niu Guangguang， et al. Effect of direct fluorination on the mechanical and scratch performance of nitrile butadiene rubber［J］. Wear，2017，376/377：1314-1320.